Título : Compósito de argamassa de cimento reforçada por fibra de sisal com entalhe definidos: caracterização mecânica e mecanismo de falha
Otros títulos : Sisal fiber reinforced cementitious mortar composite with defined notch: mechanical characterization and failure mechanism
Citación : PERES, Maria das Neves Pontes Barata. Compósito de argamassa de cimento reforçada por fibra de sisal com entalhe definidos: caracterização mecânica e mecanismo de falha. 2010. 118 f. Dissertação (Mestrado em Engenharia Mecânica) – Programa de Pós-Graduação em Engenharia Mecânica, Instituto de Tecnologia, Universidade Federal do Pará, Belém, 2010. Disponível em: http://repositorio.ufpa.br/jspui/handle/2011/5094. Acesso em:.
Resumen: Neste trabalho, foi desenvolvido um novo material compósito utilizando-se como matriz a argamassa de cimento reforçado com fibra de sisal a 1% em peso, que foram cortadas manualmente nos comprimentos de 15 mm e 25 mm utilizadas sem tratamento superficial utilizando-se o menor nível possível de processamento tecnológico nas etapas de fabricação. A pesquisa foi direcionada para estudar os mecanismos de falha desse novo material. Os compósitos foram produzidos com moldagem manual utilizando-se vibrador de imersão para melhor adensamento. Foram confeccionados corpos de prova da matriz pura e do compósito com fibra de sisal, com entalhes pré definidos, de 1,7 mm, 3,0 mm e 5,0 mm. As propriedades mecânicas foram avaliadas por ensaio de flexão em três pontos e correlacionadas com o aspecto fractográfico realizados no Microscópio Eletrônico de Varredura. Os resultados mostraram que a presença das fibras de sisal, inseridas na pasta de cimento, provocou restrição à retração plástica da mistura fresca, possivelmente pela elevada capacidade de absorção de água do reforço fibroso, um incremento na resistência mecânica e aumento da tenacidade do compósito em relação a matriz entre as séries de entalhes, diminuindo a tendência de fratura brusca.
Resumen : In this work, we developed a new composite material using as a matrix of cement mortar reinforced with sisal fibers to 1% by weight, which were manually cut into lengths of 15 mm and 25 mm used without surface treatment using the lowest possible level of technological processes in manufacturing steps. The research was conducted to study the mechanisms of failure of this new material. The composites were produced with manual molding using immersion vibrator for better densification. Specimens were fabricated of the pure base and with the composites with sisal fiber, with pre-defined slots of 1.7 mm, 3,0 mm and 5,0 mm. The mechanical properties were evaluated by a bending test at three points and correlated with the fractographic appearance made in the Scanning Electron Microscope. The results showed that the presence of sisal fibers, embedded in cement paste,plastic shrinkage caused restriction of fresh mixture, possibly due to high water absorption capacity of fibrous reinforcement, an increase in mechanical strength and increased toughness of the composite over the base between the series of notches, decreasing the tendency to sudden fracture.
Palabras clave : Material compósito
Argamassa de cimento
Sisal
Propriedade mecânica
Composite material
Cement mortar
Mechanical property
CNPq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA::PROCESSOS DE FABRICACAO
País: Brasil
Editorial : Universidade Federal do Pará
Sigla da Instituição: UFPA
Instituto: Instituto de Tecnologia
Programa: Programa de Pós-Graduação em Engenharia Mecânica
metadata.dc.rights: Acesso Aberto
Aparece en las colecciones: Dissertações em Engenharia Mecânica (Mestrado) - PPGEM/ITEC

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Dissertacao_CompositoArgamassaCimento.pdf6,47 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons