Caracterização de tintas industriais aplicadas na região amazônica a partir de análises físico-químicas, mecânicas e de durabilidade
(Universidade Federal do Pará, 2024-02-28) LUCAS, Mathaus Moraes; SILVA, Alisson Clay Rios da; http://lattes.cnpq.br/7389345867032737; https://orcid.org/0000-0001-9186-2287
In Brazil, the industrial sector of paints and varnishes is among the five largest in the market. The manufacture of paints for various applications, with technology and technical responsibility, equals the most advanced global production centers. The durability of a paint refers to its resistance to weathering. For weathering, a weather-resistant paint is necessary so that fading does not occur on the substrate where it will be used, which can occur among some factors, due to the incidence of sunlight and heavy rains. The North region, with high rainfall, influenced by instability lines, presents significant spatial and seasonal heterogeneity of rainfall and has the highest annual rainfall total. Given this reality, a paint commercially applied in the Amazon region was developed. In the standard formulation, variations of mineral loads (Kaolin, Dolomite and Precipitated Calcium Carbonate) were made and subsequently analyses and tests were carried out to evaluate the performance of this paint, compared with the original formulation, such as abrasion resistance and weathering resistance. The paint production methodology will be according to Castro (2009) using Hare’s technique (1974). The characterization of the paints in the fresh state was carried out through the Viscosity, pH and specific weight tests, while the characterization of the paints in the hardened state was carried out through the abrasion resistance tests, weathering resistance test and Scanning Electron Microscopy. The physico-chemical tests revealed that, in relation to Stormer viscosity, all formulations exceeded the standard (130 KU), with the exception of the paints containing 30% Dolomite, 15% PCC, 15% Dolomite and the ternary combination of 5% Kaolin, 5% Dolomite and 20% PCC. As for the specific weight, the formulation that came closest to the standard was the binary paint with 15% Kaolin and 15% PCC, presenting an average value of 1.43 g/cm³. In terms of pH, all formulations showed alkalinity, with values ranging between 7.5 and 9.6. After a period of exposure of 180 days, none of the mixtures, including the standard formulation, showed the formation of pathologies, demonstrating resistance to weathering. The formulations with 30% Dolomite; 15% PCC and 15% Dolomite; 5% PCC, 5% Kaolin and 20% Dolomite; 10% Kaolin, 10% PCC and 10% Dolomite, exhibited respectively 300, 290, 240, 270 cycles of abrasion resistance, indicating the potential of these paints for a variety of applications, such as floor paints, external paints and road paints.