Sílica gel obtida de escória de alto forno: Marabá, Pará
| dc.citation.issue | 359 | pt_BR |
| dc.citation.spage | 359 | pt_BR |
| dc.citation.volume | 61 | pt_BR |
| dc.creator | REBELO, Monaliza Maia | |
| dc.creator | NASCIMENTO, Lidiane Diniz do | |
| dc.creator | CORRÊA, José Augusto Martins | |
| dc.date.accessioned | 2017-05-31T19:56:52Z | |
| dc.date.available | 2017-05-31T19:56:52Z | |
| dc.date.issued | 2015-09 | |
| dc.description.abstract | Silica gel with similar properties to commercial silica was obtained from blast furnace slag (EAF) using digestion with hydrochloric acid. The EAF-silica was obtained and characterized by different techniques. The results showed that the EAF-silica obtained was amorphous, with 99.7% purity and specific area 282 m2/g. It presented high hydrophilic character (12.27%), with constitution water of ~ 6.18%, which was confirmed by mass loss in thermogravimetric analysis. The EAF-silica particles had micrometric sizes (< 1 µm) with aggregates, unimodal size distribution and D50 7.0 µm. | pt_BR |
| dc.description.resumo | Sílica gel com propriedades similares à sílica comercial foi obtida a partir de escória de alto forno (EAF), utilizando digestão com ácido clorídrico. A EAF-sílica obtida foi caracterizada por diferentes técnicas, mostrando-se amorfa, com pureza 99,7% e área específica 282 m2/g. Apresentou caráter hidrofílico alto (12,27%), com água de constituição de ~ 6,18%, o que foi confirmado pela perda de massa durante a análise termogravimétrica. As partículas de EAF-sílica apresentaram tamanhos micrométricos (< 1 µm) em forma de agregados, distribuição granulométrica unimodal e D50 7,0 µm. | pt_BR |
| dc.identifier.citation | REBELO, Monaliza Maia ; NASCIMENTO, Lidiane Diniz do ; CORREA, José Augusto Martins. Sílica gel obtida de escória de alto forno: Marabá, Pará. Cerâmica, São Paulo, v. 61, n. 359, p. 359-366, jul./set. 2015. Disponível em: <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132015000300359&lng=pt&nrm=iso>. Acesso em: 31 maio 2017. <http://dx.doi.org/10.1590/0366-69132015613601897>. | pt_BR |
| dc.identifier.issn | 1678-4553 | pt_BR |
| dc.identifier.uri | https://repositorio.ufpa.br/handle/2011/8581 | |
| dc.language | por | pt_BR |
| dc.publisher | Universidade Federal do Pará | pt_BR |
| dc.publisher.country | Brasil | pt_BR |
| dc.publisher.initials | UFPA | pt_BR |
| dc.relation.ispartof | Cerâmica | pt_BR |
| dc.rights | Acesso Aberto | pt_BR |
| dc.subject | Sílica gel | pt_BR |
| dc.subject | Polímeros Inorgânico | pt_BR |
| dc.subject | Geoquímica analítica | pt_BR |
| dc.subject | Calcinação | pt_BR |
| dc.title | Sílica gel obtida de escória de alto forno: Marabá, Pará | pt_BR |
| dc.title.alternative | Silica gel obtained from blast furnace slag: Marabá, PA, Brazil | pt_BR |
| dc.type | Artigo de Periódico | pt_BR |
| dcterms.citation.epage | 366 | pt_BR |