Por favor, use este identificador para citar o enlazar este ítem:
https://repositorio.ufpa.br/jspui/handle/2011/10359| Tipo: | Artigo de Periódico |
| Fecha de publicación : | dic-2016 |
| Autor(es): | MOTA, Carlos Alberto Mendes da NASCIMENTO, Alexandre Saldanha do GARCIA, Douglas Neves SILVA, Diego Almir Silva da TEIXEIRA, Felipe Ribeiro FERRARESI, Valtair Antônio |
| metadata.dc.description.affiliation: | MOTA, C. A. M. Dr. Docente da Universidade Federal do Pará, Instituto de Tecnologia, Faculdade de Engenharia Mecânica NASCIMENTO, A. S. Dr. Docente da Universidade Federal do Pará, Instituto de Tecnologia, Faculdade de Engenharia Mecânica GARCIA, D. N. Dr. Docente da Universidade Federal do Pará, Faculdade de Engenharia Mecânica, Campus de Tucuruí |
| Título : | Revestimento de níquel depositado pela soldagem MIG e MIG com arame frio |
| Otros títulos : | Coating welds with a nickel superalloy deposited by GMAW and GMAW cold wire |
| Citación : | MOTA, Carlos Alberto Mendes da et al. Revestimento de níquel depositado pela soldagem MIG e MIG com arame frio. Soldagem & Inspeção, São Paulo, v. 21, n. 4, p. 483-496, out./dez. 2016. Disponível em: <http://repositorio.ufpa.br/jspui/handle/2011/10359>. Acesso em:. |
| Resumen: | Este artigo apresenta um estudo das características operacionais, geométricas e microestruturais de soldas MIG e MIGAF (MIG com arame frio) aplicadas no revestimento de chapa de um aço AISI 1020, com uma superliga de níquel ER NiCrMo-4, tipo Hastelloy 276C. A soldagem foi automatizada, na posição plana, e realizada por uma fonte eletrônica em CC+ com aquisição instantânea dos oscilogramas de corrente e tensão de soldagem. As variáveis de entrada foram às velocidades do arame eletrodo e do arame frio, e a velocidade de soldagem. Foram avaliadas a operacionalidade dos processos e o efeito da energia de soldagem sobre as características geométricas (reforço e largura), diluição, microestrutura e microdureza do revestimento. Os resultados indicaram um bom desempenho operacional, a ausência de defeitos nos passes isolados e nos revestimentos para as soldagens com MIGAF. Além disso, constataram-se menores níveis de diluição. |
| Resumen : | This paper presents a study about the operational, geometrical and microstructural characteristics of GMAW and GMAW-CW (GMAW Cold Wire) welds applied on a coating of steel AISI 1020 plate, with a nickel superalloy ER NiCrMo-4, Hastelloy 276C type. The welding was automated in flat position, and executed with an electronic source on DC+ and having instantaneous acquisition of the welding voltage and current oscillograms. The input variables were the speeds of the electrode and cold wires and the welding speed. It was evaluated the operational processes and the effect of heat input on the geometrical characteristics (reinforcement and width), dilution, microstructure and microhardness of the coating. The results indicated a good operating performance, the absence of defects in single passes and in the GMAW-CW coatings. Furthermore, it has been found the lowest level of dilution. |
| Palabras clave : | Superligas de níquel Resistência de materiais Soldagem Revestimento de chapa |
| CNPq: | CNPQ::ENGENHARIAS::ENGENHARIA MECANICA |
| Series/Report no.: | Soldagem & Inspeção |
| ISSN : | 0104-9224 1980-6973 |
| País: | Brasil |
| Editorial : | Universidade Federal do Pará |
| Sigla da Instituição: | UFPA |
| metadata.dc.rights: | Acesso Aberto |
| metadata.dc.source.uri: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0104-92242016000400483&lng=pt&nrm=iso |
| metadata.dc.identifier.doi: | http://dx.doi.org/10.1590/0104-9224/si2104.08 |
| Aparece en las colecciones: | Artigos Científicos - FEM/ITEC |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| Artigo_RevestimentoNiquelDepositado.pdf | 3,11 MB | Adobe PDF | Visualizar/Abrir |