Use este identificador para citar ou linkar para este item:
https://repositorio.ufpa.br/jspui/handle/2011/8886
Tipo: | Artigo de Periódico |
Data do documento: | Dez-2015 |
Autor(es): | GOMES, Carlos Henrique Ursolino KIKUCHI, Rafael Hideo Lopes BARROS, André dos Santos SILVA, José Nazareno Santos da SILVA, Maria Adrina Paixão de Souza da MOREIRA, Antonio Luciano Seabra ROCHA, Otávio Fernandes Lima da |
Título: | On the Natural Convection in the Columnar to Equiaxed Transition in Directionally Solidified Aluminum-based Binary and Multicomponent Alloys |
Citar como: | GOMES, Carlos Henrique Ursolino et al. On the Natural Convection in the Columnar to Equiaxed Transition in Directionally Solidified Aluminum-based Binary and Multicomponent Alloys. Materiais Research, São Carlos, v. 18, n. 6, p. 1362-1371, nov./dez. 2015. Disponível em: <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392015000601362&lng=pt&nrm=iso>. Acesso em: 20 jul. 2017. Epub 04-Dez-2015. <http://dx.doi.org/10.1590/1516-1439.036315>. |
Abstract: | In order to investigate the effect of natural convection in columnar to equiaxed transition (CET), Al-3.0wt.%Cu and Al-3.0wt.%Cu-5.5wt.%Si alloys ingots were obtained during the transient horizontal directional solidification (THDS). Aiming to analyze the effect of superheat in the formation of the macrostructure in ternary Al-Cu-Si alloy, the experiments were conducted with three superheat temperatures above the liquidus temperature of the ternary alloy. A water-cooled solidification experimental device was used. Continuous temperature measurements were made during solidification at different positions in the casting and the data were automatically acquired. Thermal analysis has been applied to determine the thermal parameters such as growth rate (VL), cooling rate (TR) and temperature gradient (GL), whose values have been interrelated with the CET. The observation of the macrostructures has indicated that the resulting thermosolutal convection combined with superheat seem to favor the transition, which did not occur in a single plane, for all ingots obtained, i.e., it has been seen in a range of positions in ingots. The addition of Si element in binary Al-Cu alloy anticipates the CET. A comparison with experimental results for CET occurrence in different growth directions has been carried out. |
Palavras-chave: | Ligas de alumínio Solidificação Análise térmica Parâmetros térmicos |
Título do Periódico: | Materials Research |
ISSN: | 1980-5373 |
País: | Brasil |
Instituição: | Universidade Federal do Pará |
Sigla da Instituição: | UFPA |
Tipo de Acesso: | Acesso Aberto |
Aparece nas coleções: | Artigos Científicos - FEM/ITEC |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Artigo_NaturalConvectionColumnar.pdf | 2,9 MB | Adobe PDF | Visualizar/Abrir |
Este item está licenciado sob uma Licença Creative Commons