2016-03-142016-03-142014-06VASCONCELOS, Angela de Jesus et al. Influence of thermal parameters on the dendritic arm spacing and the microhardness of Al-5.5wt.%Sn alloy directionally solidified. Rem: Revista Escola de Minas, Ouro Preto, v. 67, n. 2, p. 173-179, jun. 2014. Disponível em: <http://www.scielo.br/pdf/rem/v67n2/07.pdf>. Acesso em: 10 mar. 2016. <http://dx.doi.org/10.1590/S0370-44672014000200007>.0370-4467https://repositorio.ufpa.br/handle/2011/7139Al-Sn alloys are widely used in tribological applications. In this study, thermal, microstructural and microhardness (HV) analysis were carried out with an Al-5.5wt.%Sn alloy ingot produced by horizontal directional transient solidification. The main parameters analyzed include the growth rate (VL) and cooling rate (TR).These thermal parameters play a key role in the microstructural formation. The dendritic microstructure has been characterized by primary dendritic arm spacing (λ1) which was experimentally determined and correlated with VL, and TR. The behavior presented by the Al-5.5wt.%Sn alloy during solidification was similar to that of other aluminum alloys, i.e., the dendritic network became coarser with decreasing cooling rates, indicating that the immiscibility between aluminum and tin does not have a significant effect on the relationship between primary dendritic arm spacing and the cooling rate. The dependence of the microhardness on VL, TR and λ1 was also analyzed. It was found that for increasing values of TR, the values of HV decrease. On the other hand, the values of HV increase with increasing values of λ1.engAcesso AbertoSolidificaçãoEspaçamento dendrítico primárioLigas Al-SnLigas de alumínioArtigo de Periódico