Por favor, use este identificador para citar o enlazar este ítem: http://repositorio.ufpa.br:8080/jspui/handle/2011/10846
Tipo: Artigo de Periódico
Fecha de publicación : nov-2017
Autor(es): MAGNO, Igor Alexsander Barbosa
SOUZA, Fabricio Vinicius Andrade de
BARROS, André dos Santos
COSTA, Marlo Oliveira
NASCIMENTO, Jacson Malcher
COSTA, Thiago Antônio Paixão de Sousa
ROCHA, Otávio Fernandes Lima da
metadata.dc.description.affiliation: MAGNO, I. A. B.; SOUZA, F. V. A.; BARROS, A. S.;NASCIMENTO, J. M.; ROCHA, O. F. L. Universidade Federa do Pará
Título : Effect of the T6 Heat Treatment on Microhardness of a Directionally Solidified Aluminum-Based 319 Alloy
metadata.dc.description.sponsorship: FAPESPA - Fundação Amazônia de Amparo a Estudos e Pesquisas
Citación : MAGNO, Igor Alexsander Barbosa et al . Effect of the T6 Heat Treatment on Microhardness of a Directionally Solidified Aluminum-Based 319 Alloy. Materials Research, São Carlos, v. 20, supl. 2, p. 662-666, 2017. Disponível em: http://repositorio.ufpa.br/jspui/handle/2011/10846. Acesso em;.
Resumen : Aluminum alloys of the ANSI series 319 present Si and Cu as the main alloying elements and the mechanical strength of these alloys can be improved by the precipitation of the metastable Al2Cu phase during the ageing heat treatment. In this paper, the Al-5.5wt.%Si-3wt.%Cu alloy was elaborated and solidified in a water-cooled horizontal directional solidification device. The as-cast ingot was subjected to the precipitation hardening heat treatment (T6 heat treatment), which consisted of: solution for 5 h at 490°C±2°C, followed by quenching in water at 60°C±2°C and ageing for 3 h at 155°C±2°C, and cooling-air. Secondary dendrite arm spacing (λ2) measurements were carried out before and after T6 heat treatment. The mechanical strength of the alloy was investigated by the microhardness test. It has been found that the heat treatment did not influence the λ2 values, however, highest HV values have been observed for the heat-treated samples.
Palabras clave : T6 Heat Treatment
Microstructure
Al-Cu-Si Alloys
Series/Report no.: Materials Research
ISSN : 1980-5373
País: Brasil
Editorial : Universidade Federal do Pará
Sigla da Instituição: UFPA
metadata.dc.rights: Acesso Aberto
metadata.dc.source.uri: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392017000800662&lang=en
metadata.dc.identifier.doi: http://dx.doi.org/10.1590/1980-5373-mr-2016-0961
Aparece en las colecciones: Artigos Científicos - ITEC

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Article_EffectTreatmentMicrohardness.pdfINGLÊS3,22 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons