Use este identificador para citar ou linkar para este item: http://repositorio.ufpa.br:8080/jspui/handle/2011/11804
Tipo: Artigo de Periódico
Data do documento: Nov-2017
Autor(es): SANTOS, Jheison Lopes dos
MONTEIRO, Sergio Neves
CÂNDIDO, Veronica Scarpini
SILVA, Anderson Oliveira da
TOMMASINI, Flavio James
ORCID do(s) autor(es): https://orcid.org/0000-0002-7075-1665
https://orcid.org/0000-0002-3926-0403
https://orcid.org/0000-0003-0936-9886
Afiliação do(s) Autor(es): CÂNDIDO, V.S. Universidade Federal do Pará, Instituto de Tecnologia (ITEC)
Título: Fracture modes of AISI type 302 stainless steel under metastable plastic deformation
Agência de fomento: CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico
FAPERJ - Fundação Carlos Chagas Filho de Amparo à Pesquisa do Estado do Rio de Janeiro
Citar como: SANTOS, Jheison Lopes dos et al. Fracture modes of AISI type 302 stainless steel under metastable plastic deformation. Materials Research, São Carlos, v. 20, p. 1-7, nov. 2017. DOI: http://dx.doi.org/10.1590/1980-5373-mr-2017-0051. Disponível em:. Acesso em:.
Resumo: A transformação martensítica pode ser induzida por deformação plástica em ligas à base de ferro metaestáveis, como aços inoxidáveis ​​contendo quantidades limitadas de C, Ni e Cr. Essa transformação ocorre na faixa de temperatura de M s e M d , geralmente em valores de temperatura relativamente mais baixos. A martensita transformada tem sido associada a força máxima máxima e ductilidade relativamente alta. No presente trabalho, as características de fratura à tração de um aço inoxidável AISI tipo 302 metaestável foram comparadas às propriedades de um aço inoxidável austenítico estável AISI tipo 310. Verificou-se que no aço 302, seu alto grau de metaestabilidade e dispersão diluída de inclusões resultam em maior resistência e modos complexos de fratura, um dos quais consistindo em inclusões globulares em torno de martensita.
Abstract: Martensitic transformation can be induced by plastic deformation in metastable iron-based alloys, such as stainless steels containing limited amounts of C, Ni and Cr. This transformation takes place at the temperature range from Ms and Md, usually at relatively lower temperature values. The transformed martensite has been associated with maximum ultimate strength and relatively high ductility. In the present work, the tensile fracture characteristics of a metastable AISI type 302 stainless steel was properties were compared to those of a stable AISI type 310 austenitic stainless steel. It was found that in 302 steel, its high degree of metastability and dilute dispersion of inclusions result in higher strength and complex modes of fracture, one of which consisting of martensite surrounding globular inclusions.
Palavras-chave: Aço inoxidável AISI tipo 302
Deformação metaestável
Transformação martensítica
Modos de fratura
AISI type 302 stainless steel
Metastable deformation
Martensitic transformation
Fracture modes
Título do Periódico: Materials Research
ISSN: 1980-5373
País: Brasil
Instituição: Associação Brasileira de Metalurgia e Materiais
Associação Brasileira de Cerâmica
Associação Brasileira de Polímeros
Sigla da Instituição: ABM
ABC
ABPol
Tipo de Acesso: Acesso Aberto
Fonte URI: http://ref.scielo.org/cbxmvq
Identificador DOI: http://dx.doi.org/10.1590/1980-5373-mr-2017-0051 
Aparece nas coleções:Artigos Científicos - ITEC

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Article_FractureModesAISI.pdf4,76 MBAdobe PDFVisualizar/Abrir


Este item está licenciada sob uma Licença Creative Commons Creative Commons