metadata.dc.type: Dissertação
Issue Date: 5-Apr-2013
metadata.dc.creator: RODRIGUES, Emerson Cardoso
metadata.dc.contributor.advisor1: MACÊDO, Emanuel Negrão
metadata.dc.contributor.advisor-co1: SOUZA, José Antônio da Silva
Title: Estudo da influência do tempo de reação e do teor de “Na” na síntese de zeólitas
Citation: RODRIGUES, Emerson Cardoso. Estudo da influência do tempo de reação e do teor de “Na” na síntese de zeólitas. 2013. 89 f. Dissertação (Mestrado) – Universidade Federal do Pará, Instituto de Tecnologia, Belém, 2011. Programa de Pós-Graduação em Engenharia Química.
metadata.dc.description.resumo: Este trabalho objetiva sintetizar zeólita tipo “A” utilizando como matéria-prima caulim de enchimento. A síntese das Zeolitas foi realizada em curto tempo e sem agitação. Os materiais de partida e o produto obtido foram identificados e caracterizados por Difração de Raios X (DRX), Espectrometria de Fluorescência de Raios X, Microscopia Eletrônica de Varredura (MEV), Análise Granulométrica e Análise Térmica Diferencial e Gravimétrica (DTA e TG). No processo de síntese foi utilizado como fonte de sílica e alumina o metacaulim, que foi calcinado na temperatura de 600 °C, por 2 horas de patamar de queima em um forno tipo mufla. Como fonte de sódio se utilizou uma solução de hidróxido de sódio 5 M, no sistema também foi adicionado água destilada. Foram realizadas diversas sínteses no interior de uma estufa a 110 °C. A variação no tempo de reação e no teor de sódio foram as variáveis estudadas no processo. Os resultados da síntese da zeólita A se mostraram satisfatório, principalmente no tempo de 10 h e com a relação Al/Na = 0,57. O tempo de reação e a quantidade de sódio são diretamente proporcionais à formação de outra fase zeolítica denominada hidroxisodalita. A partir da zeólita A, por troca iônica com uma solução de cloreto de cálcio foi possível obter a zeólita 5A sem agitação.
Abstract: This work aims to synthesize zeolite type "A" using as raw kaolin filler. The synthesis of zeolites was performed in a short time and without agitation. The starting materials and the product were identified and characterized by X ray Diffraction (XRD), Fluorescence Spectrometry, X Ray, Scanning Electron Microscopy (SEM), Grain Size Analysis and Gravimetric and Differential Thermal Analysis (DTA and TG). In the synthesis process was used as the silica source and the alumina metakaolinite, which has been calcined at a temperature of 600 ° C for 2 hours threshold firing in a muffle type furnace. As a source of sodium was used a solution of sodium hydroxide 5 M in the system was also added distilled water. Various syntheses were performed inside an oven at 110 °C. The variation in reaction time and sodium content were the variables in the process. The results of the synthesis of zeolite A proved satisfactory, especially in time of 10 h with a ratio Al / Na = 0.57. The reaction time and amount of sodium are directly proportional to the formation of another phase called zeolitic Hydroxysodalite. From the zeolite A, by ion exchange with a solution of calcium chloride was obtained zeolite 5A without agitation.
Keywords: Processo de síntese
Caulim
Metacaulim
Zeólita A
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA QUIMICA::PROCESSOS INDUSTRIAIS DE ENGENHARIA QUIMICA::PROCESSOS INORGANICOS
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal do Pará
metadata.dc.publisher.initials: UFPA
metadata.dc.publisher.department: Instituto de Tecnologia
metadata.dc.publisher.program: Programa de Pós-Graduação em Engenharia Química
metadata.dc.rights: Acesso Aberto
Appears in Collections:Dissertações em Engenharia Química (Mestrado) - PPGEQ/ITEC

Files in This Item:
File Description SizeFormat 
Dissertacao_EstudoInfluenciaTempo.pdf2,69 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons