Title: Effect of cerium loading on structure and morphology of modified Ce-USY zeolites
Citation: GARCIA, Fillipe A. C., et al. Effect of cerium loading on structure and morphology of modified Ce-USY zeolites. Journal of the Brazilian Chemical Society, São Paulo, v. 22, n. 10, p. 1894-1902, out. 2011. Disponível em: <http://www.scielo.br/pdf/jbchs/v22n10/v22n10a10.pdf>. Acesso em: 22 maio 2013. <http://dx.doi.org/10.1590/S0103-50532011001000010>.
Resumo: Este trabalho descreve detalhadamente o efeito da quantidade de cério na estrutura e morfologia da zeólita NH4USY. Ce-USY (2-25% m/m de CeO2) foi obtido por impregnação úmida de CeCl3 seguida de calcinação a 550ºC por 8 h. Em quantidades baixas (2-10%), foi observado que as espécies de cério encontram-se nas posições de troca iônica na rede, enquanto em maiores teores (15-25%) pequenos agregados formaram-se na superfície da HUSY. Difratometria de raios X (XRD) mostrou apenas reflexões relacionadas à HUSY, confirmando a alta dispersão das espécies de cério, porém as análises por espectroscopia Raman com transformada de Fourier (FT-Raman) detectaram CeOx para os materiais acima de 10%. A reação do CeCl3 com NH4USY produziu NH4Cl, o qual se decompõe em HCl, ocasionando a desaluminização da rede. Os materiais apresentaram um aumento da razão Lewis/Brønsted com o aumento da quantidade de cério, devido a interação do excesso de cério com os grupos OH da USY e consequente formação de espécies CeOx.
Abstract: This work describes comprehensibly the effect of cerium loading on the structure and morphology of NH4USY zeolite. The Ce-USY (2-25 wt.% of CeO2) was obtained by wet impregnation of CeCl3 followed by calcination at 550ºC for 8 h. At low loadings (2-10%), cerium species are mainly located at ion exchange positions in the framework, whereas at higher loadings (15-25%), small aggregates were formed on the HUSY surface. X-ray diffractograms (XRD) exhibited only the reflections related to HUSY, demonstrating the high dispersion of cerium species, but Fourier transform Raman spectroscopy (FT-Raman) detected CeOx for the materials above 10%. Reaction of CeCl3 with NH4USY produced NH4Cl, which decomposed to form HCl, leading to framework dealumination. The materials showed an increased Lewis/Brønsted ratio with increasing cerium loadings due to the interaction between the excess cerium and the OH groups of USY, and the consequent formation of CeOx species.
Keywords: Zeólita de cério USY
Óxido de cério
Troca de íons em estado sólido
Espectroscopia de Al e Si MAS NMR
ISSN: 0103-5053
Appears in Collections:Artigos Científicos - FAQUI/ICEN

Files in This Item:
File Description SizeFormat 
Artigo_EffectCeriumLoading.pdf1.4 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons