| Título: | Fracture modes of AISI type 302 stainless steel under metastable plastic deformation |
| Agência de fomento: | CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico FAPERJ - Fundação Carlos Chagas Filho de Amparo à Pesquisa do Estado do Rio de Janeiro |
| Citar como: | SANTOS, Jheison Lopes dos et al. Fracture modes of AISI type 302 stainless steel under metastable plastic deformation. Materials Research, online, v. 20, p. 1-7, nov. 2017. DOI: http://dx.doi.org/10.1590/1980-5373-mr-2017-0051. Disponível em: http://repositorio.ufpa.br/jspui/handle/2011/11804. Acesso em:. |
| Resumo: | A transformação martensítica pode ser induzida por deformação plástica em ligas à base de ferro metaestáveis, como aços inoxidáveis contendo quantidades limitadas de C, Ni e Cr. Essa transformação ocorre na faixa de temperatura de M s e M d , geralmente em valores de temperatura relativamente mais baixos. A martensita transformada tem sido associada a força máxima máxima e ductilidade relativamente alta. No presente trabalho, as características de fratura à tração de um aço inoxidável AISI tipo 302 metaestável foram comparadas às propriedades de um aço inoxidável austenítico estável AISI tipo 310. Verificou-se que no aço 302, seu alto grau de metaestabilidade e dispersão diluída de inclusões resultam em maior resistência e modos complexos de fratura, um dos quais consistindo em inclusões globulares em torno de martensita. |
| Abstract: | Martensitic transformation can be induced by plastic deformation in metastable iron-based alloys, such as stainless steels containing limited amounts of C, Ni and Cr. This transformation takes place at the temperature range from Ms and Md, usually at relatively lower temperature values. The transformed martensite has been associated with maximum ultimate strength and relatively high ductility. In the present work, the tensile fracture characteristics of a metastable AISI type 302 stainless steel was properties were compared to those of a stable AISI type 310 austenitic stainless steel. It was found that in 302 steel, its high degree of metastability and dilute dispersion of inclusions result in higher strength and complex modes of fracture, one of which consisting of martensite surrounding globular inclusions. |
| Palavras-chave: | Aço inoxidável AISI tipo 302 Deformação metaestável Transformação martensítica Modos de fratura AISI type 302 stainless steel Metastable deformation Martensitic transformation Fracture modes |
| Título do Periódico: | Materials Research |
| ISSN: | 1980-5373 |
| País: | Brasil |
| Instituição: | Associação Brasileira de Metalurgia e Materiais Associação Brasileira de Cerâmica Associação Brasileira de Polímeros |
| Sigla da Instituição: | ABM ABC ABPol |
| Tipo de Acesso: | Acesso Aberto |
| Fonte URI: | http://ref.scielo.org/cbxmvq |
| Identificador DOI: | 10.1590/1980-5373-mr-2017-0051 |
| Aparece nas coleções: | Artigos Científicos - ITEC |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| Article_FractureModesAISI.pdf | 4,76 MB | Adobe PDF | Visualizar/Abrir |
Este item está licenciado sob uma Licença Creative Commons