Título : Material compósito de matriz frágil reforçado com fibras naturais de sisal e malva: caracterização e correlações das propriedades e mecânicas
Otros títulos : Brittle matrix composite material reinforced with natural sisal and mallow fibers: characterization and correlations of properties and mechanics
Citación : MARTINS NETO, Sandoval Ferreira. Material compósito de matriz frágil reforçado com fibras naturais de sisal e malva: caracterização e correlações das propriedades e mecânicas. 2010. 94 f. Dissertação (Mestrado em Engenharia Mecânica) – Programa de Pós-Graduação em Engenharia Mecânica, Instituto de Tecnologia, Universidade Federal do Pará, Belém, 2010. Disponível em: http://repositorio.ufpa.br/jspui/handle/2011/5111. Acesso em:.
Resumen: Este estudo propõe avaliar o comportamento mecânico dos compósitos de matriz cimentícia reforçados com fibras de sisal e malva. Correlacionar o comportamento dos materiais com variação do tipo e do comprimento das fibras. O material base utilizado na fabricação do compósito foi cimento, areia, água e fibra de sisal e malva. Usou-se u traço 1 : 2 : 0,5 (cimento, areia e água), com adição de 1% de fibras em relação ao peso da mistura. As fibras foram previamente cortadas no comprimento de 15 mm e 25 mm e adicionadas manualmente à mistura. As correlações dos compósitos foram obtidos através do ensaio de flexão em três pontos, seguindo norma RILEM 49. As características micro-estruturais foram avaliadas através do uso do microscópio eletrônico de varredura.Os resultados obtidos indicam que a inserção de fibras na matriz cimentícia diminui a força máxima aplicada no corpo de prova, porém houve um ganho na tenacidade e na pseudo ductilidade do material após o aparecimento da 1ª trinca. As fibras mais longas mostraram melhor desempenho com um pequeno destaque às fibras de MALVA.
Resumen : The purpose of this thesis is evaluate the mechanical behavior of cementitious matrix composites reinforced with sisal fibers and mauve, and correlate the material’s behavior with variations in the fibers types and lengths. The base material used in the manufacture of the composite was cement, sand, water and sisal fibers and mauve. It was used the trace 1: 2: 0,5 (cement, sand and water, respectively), with the addition of 1% in mass of fibers. The fibers had been previously cut in the length of 15mm e 25mm and manually added to the mix. The correlations of the composites were obtained by bending tests in three points, following the RILEM 49 norm. The micro-structural characteristics were evaluated with electron microscopy. The results show that the insertion of fibers in the cementitious matrix reduces the maximum force applied to the specimen, even tough there was an increase in the material toughness and pseudo-ductility after the appearance of the first fissure. The longest fibers demonstrated better performance with a small highlight on the mauve fibers.
Palabras clave : Material compósito
Fibra de sisal
Fibra de malva
Matriz cimentícia
Composite material
Sisal (fiber)
Mallow fiber
Cement matrix
CNPq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA::PROCESSOS DE FABRICACAO
País: Brasil
Editorial : Universidade Federal do Pará
Sigla da Instituição: UFPA
Instituto: Instituto de Tecnologia
Programa: Programa de Pós-Graduação em Engenharia Mecânica
metadata.dc.rights: Acesso Aberto
Aparece en las colecciones: Dissertações em Engenharia Mecânica (Mestrado) - PPGEM/ITEC

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Dissertacao_MaterialCompositoMatriz.pdf3,21 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons