Use este identificador para citar ou linkar para este item:
https://repositorio.ufpa.br/jspui/handle/2011/8707| Tipo: | Artigo de Periódico |
| Data do documento: | Fev-2016 |
| Autor(es): | NEVES, Murilo Gaby LIMA, Fabrício Viana Pereira GURGEL, Júlio de Araújo VERCELINO, Célia Regina Maio Pinzan REZENDE, Fernanda Soares BRANDÃO, Gustavo Antônio Martins |
| Título: | Deflection test evaluation of different lots of the same nickel-titanium wire commercial brand |
| Citar como: | NEVES, Murilo Gaby et al. Deflection test evaluation of different lots of the same nickel-titanium wire commercial brand. Dental Press Journal Orthodontics, Maringá, v. 21, n. 1, p. 42-46, jan/fev. 2016. Disponível em: <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S2176-94512016000100042&lng=pt&nrm=iso>. Acesso em: 16 jun. 2017. <http://dx.doi.org/10.1590/2177-6709.21.1.042-046.oar>. |
| Resumo: | Introdução: o objetivo deste estudo experimental in vitro foi comparar a as propriedades elásticas da relação carga/deflexão para fios de diferentes lotes de uma mesma marca comercial. Métodos: foram selecionados quarenta segmentos de arcos de níquel-titânio superelástico (NiTi) (Morelli Ortodontia, Sorocaba/SP, Brasil), com diâmetro de 0,016”. Os grupos foram ordenados de acordo com os lotes (lotes 1, 2, 3 e 4). Foram utilizados segmentos com 28mm de comprimento da parte reta (extremidades) dos arcos pré-contornados. Os testes de deflexão foram realizados em uma máquina universal de ensaios EMIC, com célula de carga de 5N e velocidade de 1mm/minuto. A força durante a desativação foi registrada nas deflexões de 0,5; 1; 2 e 3mm. O teste de Análise da Variância (ANOVA) foi utilizado para comparar diferenças entre as médias dos grupos. Resultados: na comparação de força dos lotes em um mesmo ponto de deflexão (3, 2 e 1mm), durante a desativação, não houve diferenças estatísticas. Conclusões: não ocorre alteração nas propriedades elásticas em diferentes lotes da mesma marca. Assim, o uso de diferentes lotes dos fios ortodônticos utilizados nesta pesquisa não comprometeu o resultado final da relação carga/deflexão |
| Abstract: | Introduction: The aim of this in vitro study was to compare the elastic properties of the load-deflection ratio of orthodontic wires of different lot numbers and the same commercial brand. Methods: A total of 40 nickel-titanium (NiTi) wire segments (Morelli OrtodontiaTM - Sorocaba, SP, Brazil), 0.016-in in diameter were used. Groups were sorted according to lot numbers (lots 1, 2, 3 and 4). 28-mm length segments from the straight portion (ends) of archwires were used. Deflection tests were performed in an EMIC universal testing machine with 5-N load cell at 1 mm/minute speed. Force at deactivation was recorded at 0.5, 1, 2 and 3 mm deflection. Analysis of variance (ANOVA) was used to compare differences between group means. Results: When comparing the force of groups at the same deflection (3, 2 and 1 mm), during deactivation, no statistical differences were found. Conclusion: There are no changes in the elastic properties of different lots of the same commercial brand; thus, the use of different lots of the orthodontic wires used in this research does not compromise the final outcomes of the load-deflection ratio. |
| Palavras-chave: | Ortodontia Elasticidade Fios ortodônticos |
| Título do Periódico: | Dental Press Journal of Orthodontics |
| ISSN: | 2177-6709 |
| País: | Brasil |
| Instituição: | Universidade Federal do Pará |
| Sigla da Instituição: | UFPA |
| Tipo de Acesso: | Acesso Aberto |
| Aparece nas coleções: | Artigos Científicos - FOUFPA/ICS |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| Artigo_DeflectionTestEvaluation.pdf | 143,97 kB | Adobe PDF | Visualizar/Abrir |
Este item está licenciado sob uma Licença Creative Commons